Self-Doped Carbon Dots Decorated TiO2 Nanorods: A Novel Synthesis Route for Enhanced Photoelectrochemical Water Splitting

Herein, we have successfully prepared self-doped carbon dots with nitrogen elements (NCD) in a simple one-pot hydrothermal carbonization method, using L-histidine as a new precursor. The effect of as-prepared carbon dots was studied for photoelectrochemical (PEC) water splitting by decorating NCDs upon TiO2 nanorods systematically by changing the loading time from 2 h to 8 h (TiO2@NCD2h, TiO2@NCD4h, TiO2@NCD6h, and TiO2@NCD8h). The successful decorating of NCDs on TiO2 was confirmed by FE-TEM and Raman spectroscopy. The TiO2@NCD4h has shown a photocurrent density of 2.51 mA.cm(-2), 3.4 times higher than the pristine TiO2. Moreover, TiO2@NCD4h exhibited 12% higher applied bias photon-to-current efficiency (ABPE) than the pristine TiO2. The detailed IPCE, Mott-Schottky, and impedance (EIS) analyses have revealed the enhanced light harvesting property, free carrier concentration, charge separation, and transportation upon introduction of the NCDs on TiO2. The obtained results clearly portray the key role of NCDs in improving the PEC performance, providing a new insight into the development of highly competent TiO2 and NCDs based photoanodes for PEC water splitting.

Automated summary

In this study, self-doped carbon dots with nitrogen elements (NCD) were successfully prepared using L-histidine as a precursor through a simple one-pot hydrothermal carbonization method. The effect of NCDs on photoelectrochemical (PEC) water splitting was investigated by decorating NCDs on TiO2 nanorods. The results showed improved PEC performance with the introduction of NCDs on TiO2.