期刊
JOURNAL OF MATERIALS RESEARCH
卷 31, 期 8, 页码 1124-1132出版社
CAMBRIDGE UNIV PRESS
DOI: 10.1557/jmr.2016.103
关键词
-
资金
- National Natural Science Foundation of China [51404153]
- Shanghai Yang-fan Program [14YF1402000]
The effect of solution treatment (ST) on the microstructure and mechanical properties of cast Al-3Li-1.5Cu-0.2Zr alloy was investigated. Results showed that the volume fraction of secondary phases (Al2Cu, Al3Li) decreased obviously after ST. It was found that the strengthening of Al-3Li-1.5Cu-0.2Zr alloy was a balance of the precipitation strengthening, residual phase strengthening and fine grain strengthening. The residual phase strengthening and fine grain strengthening decreased with increasing the solution temperature and time, while precipitation strengthening increased. After ST at 560 degrees C for 40 h, the elongation of Al-3Li-1.5Cu-0.2Zr alloy reaches the highest value of 22.1%. In addition, the tensile properties are up to the highest values, ultimate tensile strength of 359 MPa and elongation of 3.5% after optimal ST at 560 degrees C for 40 h followed by aging treatment.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据