JOURNAL OF MATERIALS PROCESSING TECHNOLOGY
卷 237, 期 -, 页码 65-74出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jmatprotec.2016.06.005
关键词
Magnesium alloy; Multi-pass rolling; Microstructure; Planar anisotropy; Ductility
资金
- National Natural Science Foundation of China [51401064]
- Sci-tech Development Project in Shandong Province [2014GGX10211]
- Sci-tech Major Project in Shandong Province [2015ZDJQ02002]
Thin Mg-6.63 wt.%Zn-0.56 wt.%Zr (ZK61) magnesium alloy sheets with fine-grain structure were successfully fabricated by extrusion and multi-pass rolling with lowered temperature from 653 K to 523 K. Relationships between grain size, texture and mechanical properties of as-rolled ZK61 magnesium alloy were investigated. Microstructure homogeneity as well as planar texture anisotropy was strikingly improved by hot rolling deformation via multiple dynamic recrystallization. A uniform fine-grained structure of 6.1 mu m in average grain size and a {0002} basal texture were obtained. These led to better strength isotropy in the plane, and high yield strengths of similar to 200 MPa, which was related to pyramidal (< c+a >) slip. Enhanced ductility more than 20% in fracture elongation was composed of uniform elongation strongly correlated with basal texture, especially along TD, and post-necking elongation enhanced by grain refinement. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据