期刊
MATERIALS
卷 15, 期 19, 页码 -出版社
MDPI
DOI: 10.3390/ma15196909
关键词
sintering; composites; mechanical properties; Al2O3; MAX phases
类别
资金
- Ministry of Science and Higher Education Republic of Poland
This article describes the manufacturing process of alumina composites with the addition of titanium aluminum carbide Ti3AlC2. The composites were obtained using powder metallurgy technique with three types of mills and consolidated through Spark Plasma Sintering method. The influence of the Ti3AlC2 addition on the microstructure and mechanical properties of the composites was analyzed, and the structure of the MAX phase after the sintering process was investigated.
This article describes the manufacturing of alumina composites with the addition of titanium aluminum carbide Ti3AlC2, known as MAX phases. The composites were obtained by the powder metallurgy technique with three types of mill (horizontal mill, attritor mill, and planetary mill), and were consolidated with the use of the Spark Plasma Sintering method at 1400 degrees C, with dwelling time 10 min. The influence of the Ti3AlC2 MAX phase addition on the microstructure and mechanical properties of the obtained composites was analyzed. The structure of the MAX phase after the sintering process was also investigated. The chemical composition and phase composition analysis showed that the Ti3AlC2 addition preserved its structure after the sintering process. The increase in fracture toughness for all series of composites has been noted (over 20% compared to reference samples). Detailed stereological analysis of the obtained microstructures also could determine the influence of the applied mill on the homogeneity of the final microstructure and the properties of obtained composites.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据