JOURNAL OF MATERIALS PROCESSING TECHNOLOGY
卷 229, 期 -, 页码 514-519出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jmatprotec.2015.09.038
关键词
Semisolid; A356 alloy; Squeeze casting; Microstructure; Properties
资金
- National Natural Science Foundation for Outstanding Young Scholars of China [51222405]
- National Natural Science Foundation of China [51474063]
The microstructures of A356 alloy parts contained near-round or rosette alpha-Al grains and eutectics at grain boundaries. Melt processing by vibrating slope could refine grain size and eliminate eutectic phase segregation as well as regional segregation which usually occurred in traditional squeeze casting. Average grain diameter of alpha-Al grain increased from 44 gm to 6411111, and grain average roundness decreased firstly from 2.9 to 1.7 then increased to 3.3 with the increase of casting temperature. At casting temperature from 670 degrees C to 680 degrees C, crack and cooling shut usually occurrectin the products due to poor flow ability of the alloy. When the casting temperature was 690 degrees C, the alloy had a good filling ability and smooth product with fine near-round or rosette alpha-Al grains and homogenous eutectics has been obtained. The ultimate tensile strength and elongation of semisolid squeeze casting A356 alloy reached 232 MPa and 7%, which were improved by 12% and 21% respectively as comparing with that of traditional squeeze casting. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据