JOURNAL OF MATERIALS ENGINEERING AND PERFORMANCE
卷 25, 期 5, 页码 1974-1985出版社
SPRINGER
DOI: 10.1007/s11665-016-2041-4
关键词
bio-corrosion; corrosion residual strength; high strain rate rolling; microstructure; wrought magnesium alloy
资金
- Natural Science Foundation Project of China [51571089]
- Hunan University [531107021095]
- National SIT Project
Microstructure, bio-corrosion behavior, and corrosion residual strength in 0.9 wt.% NaCl solution of the fine-grained Mg-4Zn alloy sheet prepared by high strain rate rolling are systematically investigated. The as-rolled alloy has fine homogenous dynamic recrystallization grains with the average grain size of 4.5 mu m. It has different bio-corrosion behavior from the as-cast and is the most corrosion resistant except for pure Mg. Its in vitro strength loss is about 19% after 7 days immersion (the as-cast, 62%), and corrosion residual strength after 15 days immersion is 205 MPa. Its in vitro strength loss after 15, 30, and 60 days immersion are 24, 37, and 38% respectively. The as-rolled Mg-4Zn alloy is featured with the slighter in vitro loss of mechanical integrity due to uniform bio-corrosion and is desirable for the usage in the field of bone fixation.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据