JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 401, 期 -, 页码 1145-1149出版社
ELSEVIER
DOI: 10.1016/j.jmmm.2015.11.025
关键词
Heusler alloys; Magneto-structural transitions; Thermoelectricity; Multifunctional
资金
- Office of Basic Energy Sciences, Material Science Division of the U.S. Department of Energy, DOE [DE-FG02-06ER46291, DE-FG02-13ER46946]
- Russian Foundation for Basic Research [15-02-01976]
The crystal structure, magnetic and transport properties, including resistivity and thermopower, of NisoMnis 75Cu6.25Ga25 and Ni49.80Mn34.66In15.54 Heusler alloys were studied in the (10-400) K temperature interval. We show that their physical properties are remarkably different, thereby pointing to different origin of their magnetostructural transition (MST). A Seebeck coefficient (S) was found to pass minimum of about -20 mu V/K in respect of temperature for both compounds. It was shown that MST observed for both compounds results in jump-like changes in S for Ga-based compound and jump in resistivity of about 20 and 200 mu Omega cm for Ga and In -based compounds, respectively. The combined analyzes of the present results with that from literature show that the density of states at the Fermi level does not change strongly at the MST in the case of Ni-Mn-In alloys as compared to that of Ni-Mn-Ga. (C) 2015 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据