期刊
JOURNAL OF MAGNETISM AND MAGNETIC MATERIALS
卷 408, 期 -, 页码 147-151出版社
ELSEVIER
DOI: 10.1016/j.jmmm.2016.02.061
关键词
Nanoferrites; Rare-earth metals; XRD; FTIR; Coercivity; Saturation magnetization
资金
- Deanship of Scientific Research at King Saud University [PRG-1436-25]
Rare-earth (RE=La3+,Nd3+,Gd3+,Tb3+,Dy3+) doped Ba2NiCoRExFe28- xO46 (x=0.25) hexagonal ferrites were synthesized for the first time via micro-emulsion route, which is a fast chemistry route for obtaining nano-sized ferrite powders. These nanomaterials were investigated by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), as well as vibrating sample magnetometer (VSM). The XRD analysis exhibited that all the samples crystallized into single X-type hexagonal phase. The crystalline size calculated by Scherrer's formula was found in the range 7-19 nm. The variations in lattice parameters elucidated the incorporation of rare-earth cations in these nanomaterials. FTIR absorption spectra of these X-type ferrites were investigated in the wave number range 500-2400 cm(-1) Each spectrum exhibited absorption bands in the low wave number range, thereby confirming the X-type hexagonal structure. The enhancement in the coercivity was observed with the doping of rare-earth cations. The saturation magnetization was lowered owing to the redistribution of rare-earth cations on the octahedral site (3bvi). The higher values of coercivity (664-926 Oe) of these nanomaterials suggest their use in longitudinal recording media. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据