Aqueous zinc-ion battery; MnO/C; Morphology design; H+/Zn2+ co-insertion
资金
- National Natural Science Foundation of China [22078200, 51874199]
- Guangdong Basic and Applied Basic Research Foundation [2021A1515010162]
In this study, a two-dimensional MnO/C composite derived from MOF was prepared and demonstrated to exhibit high cyclic stability and capacity retention at different current densities, providing a new approach for the development of high-performance AZIBs cathode with controllable morphology.
Poor conductivity, sluggish ion diffusion kinetics and short cycle life hinder the further development of manganese oxide in aqueous zinc-ion batteries (AZIBs). Exploring a cathode with high capacity and long cycle life is critical to the commercial development of AZIBs. Herein, a two-dimensional (2D) MnO/C composite derived from metal organic framework (MOF) was prepared. The 2D MnO/C cathode exhibits a remarkably cyclic stability with the capacity retention of 90.6% after 900 cycles at 0.5 A.g(-1) and maintains a high capacity of 120.2 mAh.g(-1) after 4500 cycles at 1.0 A.g(-1). It is demonstrated that MnO is converted into Mn3O4 through electrochemical activation strategy and shows a Zn2+ and H+ co-intercalation mechanism. In general, this work provides a new path for the development of high-performance AZIBs cathode with controllable morphology.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据