Single-phase far-red-emitting CaAl12O19:x%Cr3+ phosphors were successfully synthesized using a sol-gel method. The optimized phosphors exhibit excellent optical properties and have the potential to be used in violet-pumped plant growth LEDs.
Single-phase far-red-emitting CaAl12O19:x%Cr3+ (x = 0.1 - 3.0 mol%) phosphors were successfully synthesized by a sol-gel method. Besides a small absorption peak at 263 nm, the phosphors have two broad excitation bands in the UV-blue (350 - 475 nm) and green-red (500 - 600 nm) regions, centered at 414 and 573 nm, respectively. They give a broad emission band in the 650 - 800 nm range and several narrow emission peaks at 665, 688, 695, 700, and 709 nm under violet (414 nm) and orange (573 nm) excitations. The optimum annealing temperature and doping concentration of Cr3+ ions are 1500 degrees C and 0.3%, respectively. Further, the optimized CAO: 0.3% Cr3+ phosphor exhibits an excellent color purity of 100%, activation energy of 0.4 eV, a long lifetime of 4.2 ms, and good quantum efficiency of 46.2%. A prototype of plant growth LED with the CIE coordinate of (x = 0.3050; y = 0.1264) was fabricated by coating CaAl12O19:0.3%Cr3+ phosphor on a violet (410 nm) LED chip. The ob-tained EL spectrum of plant growth LED is well-matched with the far red phytochrome (PFr) absorption spectra, demonstrating that CaAl12O19:Cr3+ is a potential far-red-emitting phosphor for violet-pumped plant growth LEDs.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据