Tuning Strong Metal-Support Interaction Kinetics on Pt-Loaded TiO2 (110) by Choosing the Pressure: A Combined Ultrahigh Vacuum/Near-Ambient Pressure XPS Study

Pt catalyst particles on reducible oxide supports often change their activity significantly at elevated temperatures due to the strong metal-support interaction (SMSI), which induces the formation of an encapsulation layer around the noble metal particles. However, the impact of oxidizing and reducing treatments at elevated pressures on this encapsulation layer remains controversial, partly due to the pressure gap between surface science studies and applied catalysis. In the present work, we employ synchrotron-based near-ambient pressure X-ray photoelectron spectroscopy (NAP-XPS) to study the effect of O-2 and H-2 on the SMSI-state of well-defined Pt/TiO2(110) catalysts at pressures of up to 0.1 Torr. By tuning the O-2 pressure, we can either selectively oxidize the TiO2 support or both the support and the Pt particles. Catalyzed by metallic Pt, the encapsulating oxide overlayer grows rapidly in 1 x 10(-5) Torr O-2, but orders of magnitude less effectively at higher O-2 pressures, where Pt is in an oxidic state. While the oxidation/reduction of Pt particles is reversible, they remain embedded in the support once encapsulation has occurred.

Automated summary

In this study, the effect of O-2 and H-2 on Pt/TiO2(110) catalysts was investigated using synchrotron-based near-ambient pressure X-ray photoelectron spectroscopy. The results showed that the rate of formation of the encapsulating oxide layer on Pt particles varied with different O-2 pressures, and once encapsulation occurred, Pt particles remained embedded in the support.