Pure Ni-Zn ferrites were synthesized using the precursor-combustion method. The results showed that the lattice parameter increased and porosity decreased with the rise in zinc substitution. Resistivity increased with zinc content, while dielectric properties were influenced by frequency and temperature. The magnetization increased up to x = 0.5 and x = 0.3 for saturation magnetization and remanent magnetization, respectively, followed by a decrease. The highest specific capacitance was observed for the composition x = 0.3.
Pure Ni-Zn ferrites were prepared by the precursor-combustion method using Ni1-xZnxFe2(C4H4O4)(3).6N(2)H(4) (x = 0.1, 0.3, 0.5, 0.7, 0.9) precursors. The fascinating property of this synthesis route is that when a small portion of the precursor is ignited, the bulk rapidly undergoes catalytic auto-decomposition forming nanoferrites. The chemical analysis of precursors confirms the presence of expected elements with desired stoichiometric ratio and thermal analysis helped to fix the formula of the precursors. The powder X-ray diffraction (XRD) studies indicated an increase in the lattice parameter (a) and a decrease in porosity (%P), with the rise in zinc substitution. The crystallite size varied from 31 to 42 nm. Scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HR-TEM) images displayed particles having cuboidal geometry. The synthesized semiconducting ferrites demonstrated an increase in resistivity with an increase in zinc content. Dielectric studies showed a significant influence of frequency and temperature on the dielectric properties with the addition of zinc. AC susceptibility studies showed particle domains changing from single domain-superparamagnetic to superparamagnetic type with the rise in zinc content. Vibrating magnetometer sample (VSM) measurements reveal an increase in the saturation magnetization (M-s) and remanent magnetization (M-r) up to x = 0.5 and x = 0.3, respectively, followed by a decrease however coercivity (H-c) showed a continuous decrease with zinc addition. The blocking temperature (T-B) depicted a decline with an increase in the zinc concentration. The electrochemical analysis exhibited the highest specific capacitance (C-sp) of 67.1 F/g for the composition x = 0.3 at the lowest scan rate.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据