A novel nanocomposite consisting of CoLa/LaH and LaH nanoparticles was synthesized and showed improved magnetic measurements. The nanocomposite displayed a higher operating frequency and could be potentially used in magnetic targeting and separators.
A novel nanocomposite consisting of 0.3 cobalt lanthanum nanoferrite/0.7 lanthanum perovskite-hematite nanoparticles (CoLa/LaH) and lanthanum perovskite-hematite nanoparticles (LaH) was synthesized using a simple method. The crystallite size was determined by the X-ray diffraction (XRD) pattern, and the particle size was determined using atomic force microscopy (AFM) to demonstrate that the nano-samples had sizes within the nanoscale range. Fourier transform infrared analysis was utilized to ensure that the nano-samples were formed. By adding CoLa nanoferrite to the LaH nanoparticles, an improvement in magnetic measurements was observed. The saturation magnetization of the CoLa/LaH nanocomposite was 1.1-fold larger than that of LaH. Also, the CoLa/LaH coercivity was 1.7-fold higher than in LaH. Furthermore, the CoLa/LaH nanocomposite displayed a higher operating high frequency of 8.9 GHz, which could be used in an X-band super-high microwave frequency, than the LaH nanoparticles. The LaH nanoparticles, on the other hand, demonstrated a high operating frequency of 8.2 GHz, which could be used in the C-band super-high microwave frequency. No activity was observed for the investigated samples against the tested microorganisms, which was unexpected behavior. Therefore, the investigated nano-samples are interesting for being applied in magnetic targeting and separators, in particular the CoLa/LaH nanocomposite.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据