IRONMAKING & STEELMAKING
卷 50, 期 5, 页码 538-547出版社
TAYLOR & FRANCIS LTD
DOI: 10.1080/03019233.2022.2128403
关键词
Iron coke; hydrogen-rich blast furnace; softening-melting; charge structure; mixed burden
The effects of iron coke application in a hydrogen-rich blast furnace atmosphere on the softening and melting performance of burden were studied. The suitable hydrogen content was found to be 10vol.-%. The application of iron coke promoted iron ore reduction and carburizing, decreased melting and dripping temperatures, improved charge permeability, and reduced coke dissolution loss.
The effects of the application of iron coke in hydrogen-rich blast furnace atmosphere on the softening and melting performance of burden were studied.The results indicated that with the increase in hydrogen content, the cohesive zone of mixed burden became narrower and the permeability of charge was improved, and the suitable hydrogen content was 10vol.-%. The application of iron coke could promote the iron ore reduction and carburizing of iron, decrease the melting temperature by 1-10 degrees C, decrease the dripping temperature by 5-16 degrees C, narrow the cohesive zone, improve the air permeability with S value decrease of 3.19-13.87 kPa degrees C, and reduce the dissolution loss of coke and ensure the skeleton function of coke. The suitable burden structure was confirmed as follows, i.e. the ratio of pellets and sinter is 4:6, and the ratio of iron coke and coke is 2:8.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据