Study on the Flammability, Crystal Behaviors and Mechanical Performance of Polyamide 11 Composites by Intercalated Layered Double Hydroxides

期刊

出版社

MDPI
DOI: 10.3390/ijms232112818

关键词

flammability; polyamide 11; layered double hydroxides; crystal behaviors

资金

  1. Open Project Program of Engineering Laboratory of Nonhalogen Flame Retardants for Polymers (Beijing Technology and Business University, China) [BTBUFR20-7]

向作者/读者索取更多资源

In this study, sulfamic acid-intercalated MgAl-LDH (SA-LDH) was prepared and incorporated into polyamide 11 (PA11) to enhance flame retardancy and mechanical properties. The results showed that SA-LDH could effectively decrease heat release rate, induce the formation of new crystal forms, and improve compatibility between SA-LDH and PA11.
Sulfamic acid-intercalated MgAl-LDH (SA-LDH) was prepared by an anion exchange method, and its structure was characterized by X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR). SA-LDH was introduced into polyamide 11 (PA11) by melt blending and to enhance the flame retardancy and mechanical properties. The scanning electron microscope (SEM) and XRD data showed that the lamellar structure of SA-LDH was partly disrupted. The cone calorimeter (CCT) results demonstrated that SA-LDH could effectively decrease the value of heat release rate, which may be ascribed to the better distribution of SA-LDH compared to LHD in the PA11 matrix. The effects of SA-LDH on the crystal behaviors of PA11 were investigated by XRD and differential scanning calorimetry (DSC), indicating that SA-LDH could induce the formation of new crystal forms and served as a heterogeneous nucleating agent. The mechanical progress caused by the incorporation of SA-LDH was correlated with compatibility improvement between SA-LDH and PA11.