期刊
INTERNATIONAL JOURNAL OF HYDROGEN ENERGY
卷 47, 期 87, 页码 36843-36849出版社
PERGAMON-ELSEVIER SCIENCE LTD
DOI: 10.1016/j.ijhydene.2022.08.260
关键词
Electroless deposition; Platinum; Palladium; Catalysts; Hydrogen removal
资金
- Deanship of Scientific Research at King Khalid University
- [RGP.1/318/43]
This work focuses on platinum and palladium-based autocatalytic plates for hydrogen removal. The results showed that the catalytic plates coated with alumina exhibit higher catalytic efficiency compared to those without alumina coating. Among the different coating ratios, Pt 90%: Pd 10% shows the best performance.
This work focused on platinum and palladium-based autocatalytic plates, which used to remove hydrogen. The six sandblasted stainless steel plates were coated with platinum and palladium metals using the electroless coating method. The three plates A-01, A-02, A-03 were first coated with alumina using the sol-gel dip method, and after that, different ratios of platinum and palladium were deposited on them. The three other plates, B-01, B-02, B-03 (without alumina coated), were coated directly with different ratios of platinum and palladium. The platinum and palladium ratio used for coating these plates were Pt 80%: Pd 20%; Pt 90%: Pd 10%, and Pt 70%: Pd 30. The coating of these plates was charac-terized using Scanning Electron Microscopy, X-rays Fluorescence Spectroscopy, and their catalytic efficiency was measured by the Passive Autocatalytic Recombiner testing rig method. It was found that the plates coated with alumina using two dipping cycles are suitable for different coating of mixed metals by electroless coating method compared to three dipping cycles. It was observed that the alumina-coated catalytic plates (A-01, A-02, A-03) exhibited excellent catalytic efficiency as compared to those without alumina-coated plates (B-01, B-02, B-03). Furthermore, the catalytic efficiency of A-03 and B-03 is higher than other plates. It was also found that the catalytic efficiency of A-03 is higher than B-03. The best coating ratio is Pt 90%: Pd10%, and alumina-coated plates give excellent results.(c) 2022 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据