Influence of specimen orientation on fatigue crack growth in 7050-T7451 and 2050-T8 aluminium alloys

The effect of L-T and S-T orientations on FCGR is here in studied in 7050-T7451 and 2050-T8 aluminum alloys. The Low-cycle fatigue tests and hardness measurements have shown that specimen orientation has a minor effect on material plastic hardening. Lower FCG rates are obtained for both materials in the L-T orientation, which can be associated to the resistance at grain boundaries. The larger cyclic plastic zone attained in the L-T direction leads to an increase of the plasticity inducing crack closure. Crack deflection observed for L-T direction also affects the FCGR due to roughness inducing crack closure, longer crack path and lower effective delta K.

Automated summary

The effect of L-T and S-T orientations on FCGR in 7050-T7451 and 2050-T8 aluminum alloys is studied. Lower FCG rates are obtained in the L-T orientation, which can be attributed to increased resistance at grain boundaries. Additionally, crack deflection observed in the L-T direction also affects the FCGR.