Iron oxide; Papaya; Nanomaterial; Photocatalyst; Antioxidant
In this study, Fe2O3 nanoparticles coated with papaya fruit extract were synthesized and characterized. The results showed that these nanoparticles have antibacterial activity, radical scavenging activity, and dye degradation ability.
In this work, C. papaya fruit extract coated Fe2O3 NPs were green synthesized and bio-physically characterized by UV-visible spectroscopy (UV-vis), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Scanning electron microscopy (SEM) and Energy dispersive X-ray (EDX) techniques. In UV-vis spectroscopy, the absorbance spectra of Fe2O3 NPs were recorded at 300-700 nm. A strong absorbance peak was noticed at 346 nm. XRD was employed to determine the crystalline form of NPs using powdered X-ray diffractometer. XRD reflected the pure crystalline form of NPs and the crystallite size measured 7.8 nm. The presence of various functional chemical groups in the reduction process was observed by FTIR spectroscopy from 4000 to 400 cm-1. SEM and EDX of Fe2O3 NPs were performed using Hitachi S-4500 (Germany). SEM analysis revealed the presence of agglomerated NPs. The mean size of Fe2O3 NPs was 23.7 nm. The presence of elemental Fe was 51.06 % and O was 28.97 % as recorded in EDX analysis. The antibacterial effects of Fe2O3 NPs were evaluated against Gram-positive (B. subtilis and S. pyogenes) and Gram-negative (P. aeruginosa and E. coli) bacteria by agar well diffusion method. Dimethyl sulfoxide (DMSO) was used as negative control while tetracycline was used as positive con-trol. Fe2O3 NPs have significantly inhibited Gram-negative bacteria. The inhibition of E. coli was 20.2 mm at 100 mu g mL-1. The inhibition was 17.5 mm at 100 mu g mL-1 for P. aeruginosa. Fe2O3 NPs exhibited radical scavenging activity against hydrogen peroxide (H2O2). The percentage scavenging of H2O2 was enhanced to 90 % at 100 mu g mL-1. Moreover, the as synthesized Fe2O3 NPs at 1 mM concentration efficiently degraded methyl orange (MO) dye and was noticed by the reduction in the absorbance peak at 375 nm within 4 h of reaction compared to 0.5 mM Fe2O3 NPs. The results suggested that the synthesized Fe2O3 NPs could be used to treat microbial infections and oxidative damage. Further, Fe2O3 NPs may be used as a better biocatalyst for the removal of harmful in-dustrial dyes from the environment.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据