The electrical impedance of carbon xerogel hierarchical electrodes

Many electrodes used in energy storage devices are produced by grinding a micro-and meso-or macro-porous material into a powder and depositing it on a flat substrate, which leads to a hierarchical structure. At the largest scale the structure is that of a flat layer; the intermediate structure is that of porous grains; the smallest scale is that of the microporous skeleton that makes up the grains.The paper uses electrical impedance spectroscopy to investigate both experimentally and through math-ematical modelling how electric charges are stored and transported in such structure. The paper focuses on electrodes produced with a variety of carbon xerogels soaked with KCl solutions. Nonane adsorption is used during the electrode preparation to selectively block the micropores, and discriminate their contribution from that of larger pores. The impedance data are analysed with a mathematical model built on the Poisson- Boltzmann equation for charge storage and on the Nernst-Planck equation for ion transport, which accounts for the hierarchical structure of the electrodes.The equilibrium charge storage in large pores is found to be quantitatively described by the classical electric double layer. In micropores, however, non-ideality of the electrolyte has to be invoked to account for the measured capacitance, hinting at ion desolvation. As for the charge transport, each structural level is found to have a characteristic frequency, above which the storage of electric charges is transport-limited at the considered scale. The hierarchical structure of the electrode is responsible for salient characteristics of the impedance. In particular the Warburg regime, with impedance proportional to (i!)-1/2, is observed when transport is rate-limiting at one scale only. In hierarchical electrodes, an additional regime is observed with impedance proportional to (i!)-1/4 when transport limitations are present at two scales simultaneously.

Automated summary

This paper investigates the storage and transport of electric charges in electrodes with hierarchical structures using electrical impedance spectroscopy. The hierarchical structure of the electrode is found to have significant effects on the impedance due to different characteristic frequencies at each structural level. Additionally, the non-ideality of the electrolyte in micropores is found to influence the measured capacitance.