期刊
CERAMICS INTERNATIONAL
卷 49, 期 2, 页码 2591-2599出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2022.09.239
关键词
PLZST; Antiferroelectric; Low-temperature sintering; Energy storage
By adding the BASK glass phase into PLSZST ceramics, the sintering temperature was reduced, and high recoverable energy density and efficiency were achieved, making it suitable for pulsed power electronic devices.
PLZST-based antiferroelectric (AFE) ceramics with high recoverable energy density (Wre) and efficiency (eta) can be applied to pulsed power electronic devices. However, this application is constrained by the high sintering temperature (ST, 1250-1320 degrees C) of the ceramics per se. In this context, this study introduced a new glass phase of Ba2CO3-Al2O3-SiO2-K2CO3 (BASK) into Pb0.95La0.02Sr0.02(Zr0.50Sn0.40Ti0.10)O3 (PLSZST) AFE ceramics by using a traditional solid-state method. By doping 0.5 wt% BASK, the ST of PLSZST ceramics was significantly reduced from 1300 degrees C to 1020 degrees C and a high Wre of 3.54 J/cm3 and a high eta of 86% were yield, when the electric breakdown strength increased to 230 kV/cm. In addition, a pulse discharge energy density of 2.47 J/cm3, and an extremely fast discharge speed (<0.5 mu s), as well as acceptable thermal stabilities of both Wre and eta within 30-110 degrees C temperature range, were achieved. Conclusively, this AFE ceramic composition with glass additives has a great potential to be used in base metal inner-electrode multilayer ceramic capacitors for pulse power applications.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据