卷 48, 期 24, 页码 36490-36499出版社
ELSEVIER SCI LTD
DOI: 10.1016/j.ceramint.2022.08.209
关键词
Lithium-ion batteries; LiNi0.5Mn1.; Codoping; Unannealing process
资金
- Major Science and Technology Research of Guangxi Department of Funded Projects
- [1114022-15]
This study prepared single-crystal LNMO particles and Y, Ti-doped LiNi0.45Mn1.45O4 particles using a sol-gel method under different annealing processes, and compared their structural and electrochemical performance through various analytical techniques. The results showed that the doped and unannealed samples had the largest amount of disordered structures and oxygen vacancies, exhibiting excellent electrochemical performance in terms of Coulombic efficiency and specific capacity after multiple cycles.
In recent years, due to the rising price of cobalt, people have been increasingly interested in LiNi0.5Mn1.5O4 (LNMO) cathode materials, and many studies researches have been carried out on the preparation and modifi-cation of LNMO. However, the codoping of Y and Ti and the choice of annealing and unannealing processes after doping are less explored. In this study, single-crystal LNMO particles and Y, Ti-doped LiNi0.45Mn1.45O4 particles were prepared by a simple sol-gel method under annealing and unannealing processes, respectively. Four samples were analyzed by X-ray powder diffraction, Raman spectra, Fourier transform infrared spectroscopy and electron paramagnetic resonance. By these means, it was found that the samples doped and not annealed had the largest amount of disordered structures and oxygen vacancies (OVs). Scanning electron microscopy showed that the doped and unannealed samples had more exposed (100) crystal planes than the other samples, and after multiple cycles, this sample had the smoothest surface morphology. Electrochemical tests show that the doped and unannealed samples exhibit excellent electrochemical performance, with a Coulombic efficiency of 93.94% in the first cycle, a specific capacity of 126.74 mAh.g(-1) after 500 cycles at a rate of 1 C, and a specific capacity of 126.74 mAh.g(-1) at a rate of 5 C. After 500 cycles, the specific capacity is 111.1 mAh.g(-1).
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据