In this study, CoFe-based oxide nanosheets were prepared and used as catalysts for the thermal decomposition of ammonium perchlorate (AP). The results showed that the CoFe-based oxide nanosheets significantly reduced the decomposition temperature and apparent activation energy of AP, providing a new approach for the preparation and application of functional materials in the field of energetic materials.
In this work, CoFe-based oxide nanosheets were prepared by a facile method and its catalysis effects on the thermal decomposition of ammonium perchlorate (AP) were studied. CoFe-based oxide nanosheets were obtained from hydrothermal process and high-temperature treatment of CoFe-layered double hydroxide. The samples were characterized by scanning electron microscopy and high-resolution transmission electron microscopy. The thermal catalytic decomposition of AP with CoFe-based oxide nanosheets as catalysts was investigated by differential scanning calorimetry and coupling Fourier transform infrared spectrometer. The results showed that the CoFe-based oxide samples with the width size of 200-300 nm and the thickness size of similar to 10 nm show the inherent catalytic ability. With 10 wt% of CoFe-based oxide nanosheets added, the decomposition temperature of AP was reduced by 127.5 degrees from 431.0 degrees to 303.5 degrees. The apparent activation energy was decreased by 61.1 kJ/mol from 177.3 kJ/mol of raw AP to 116.2 kJ/mol of AP with 10 wt% of CoFe-based oxide nanosheets added. The thermal catalysis decomposition mechanism of AP with CoFe-based oxide nanosheet material promoting was proposed. This work offered a novel idea toward preparation and application of functional material layered double hydroxide in the field of energetic materials.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据