Regeneration of Exhausted Palladium-Based Membranes: Recycling Process and Economics

The aim of the present work is the recycling treatment of tubular alpha-Al2O3-supported ceramic membranes with a Pd/Ag selective layer, employed in hydrogen production with integrated CO2 capture. A nitric acid leaching treatment was investigated, and recovered ceramic supports were characterized, demonstrating their suitability for the production of novel efficient membranes. The main objective was the metal dissolution that preserved the support integrity in order to allow the recovered membrane to be suitable for a new deposition of the selective layer. The conditions that obtained a satisfactory dissolution rate of the Pd/Ag layer while avoiding the support to be damaged are as follows: nitric acid 3 M, 60 degrees C and 3.5 h of reaction time. The efficiency of the recovered supports was determined by nitrogen permeance and surface roughness analysis, and the economic figures were analysed to evaluate the convenience of the regeneration process and the advantage of a recycled membrane over a new membrane. The experimentation carried out demonstrates the proposed process feasibility both in terms of recycling and economic results.

Automated summary

The aim of this study was to recycle ceramic membranes with a Pd/Ag selective layer by nitric acid leaching treatment, preserving the support integrity and allowing for a new deposition of the selective layer. The feasibility of the proposed process in terms of recycling and economic results was demonstrated through experimentation.