TBC; ZrO2-YO1.5-NbO2.5; Thermal conductivity; Laser
资金
- Coordenaca~o de Aperfeicoamento de Pessoal de Ni'vel Superior-Brazil (CAPES) [001]
This study investigated the thermal conductivity properties of zirconia ceramic for thermal barrier coating (TBC) application. It was found that zirconia co-doped with yttria and niobia significantly reduced the thermal conductivity and could be a potential thermal insulation material for TBC application.
The reduction of thermal conductivity provided by the zirconia ceramic for TBC application improves protection of turbine blades during the thermal cycles and the high temperature operations. The TBC is a complex system composed of different layers: a metal substrate, a metallic bond coat, thermally grown oxide (TGO), and ceramic top coat. The present study determined thermal conductivity properties by theoretical calculation of the thermal diffusivity, measured by laser flash technique, at 800 degrees C and 1250 degrees C for ZrO2-YO1.5-NbO2.5 (TC) with 14.5, 16.0, and 17.5 mol% equimolar yttria and niobia in zirconia, by CO2 laser on the substrate of titanium. Although microscopy and EDS showed that specific parameters of the laser parameters must be defined to lager thickness of the TBC layers, zirconia co-doped with yttria and niobia promoted a significant reduction of the thermal conductiv-ity by approximately 52 % when compared to zirconia with 7.6 % molar with yttria, currently used in gas turbine engine industry. That TC composition with laser processing could be explored as a candidate thermal insulation material for TBC application. (C) 2022 The Authors. Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据