Synthesis and Characterization of Monodispersed Spherical Calcium Oxide and Calcium Carbonate Nanoparticles via Simple Pyrolysis

In this study, calcium carbonate nanoparticles (CCNPs) and calcium oxide nanoparticles (CONPs) are synthesized by the carbonization/calcination of calcium oleate. CONPs are an essential inorganic material, and they are used as catalysts and as effective chemisorbents for toxic gases. CCNPs are widely used in plastics, printing ink, and medicines. Here, calcium oleate is used as a starting material for the preparation of CCNPs and CONPs. This calcium oleate is prepared from calcium hydroxide and oleic acid in ethanol under mild reflux conditions. The effect of the calcination temperature of calcium oleate is examined during the synthesis of CCNPs and CONPs. By simple carbonization/calcination, calcite-type CCNPs and CONPs are prepared at 600 degrees C, respectively. The synthesized nanomaterials are analyzed by various physicochemical characterization techniques such as X-ray diffraction (XRD), Fourier transform infrared spectroscopy, thermogravimetric analysis (TGA) with derivative thermogravimetry (DTG), and scanning electron microscopy (SEM) with energy dispersive X-ray analysis. An X-ray diffractometer and the Scherrer formula are used to analyze the crystalline phase and crystallite size of prepared nanoparticles. TGA techniques confirm the thermal stability of the calcium oleate, CCNPs, and CONPs. The SEM analysis illustrates the dispersive behavior and cubic/spherical morphologies of CCNPs/CONPs. Furthermore, the obtained results are compared to the CCNP and CONP samples prepared using calcium hydroxide. As a result, the carbonization/calcination of calcium oleate produces monodispersed CONPs, which are then compared to the CONPs from calcium hydroxide. Additionally, from calcium oleate, CONPs can be prepared on a large scale in a cheap, convenient way, using simple equipment which can be applied in various applications.

Automated summary

In this study, calcium carbonate nanoparticles (CCNPs) and calcium oxide nanoparticles (CONPs) were synthesized through the carbonization/calcination of calcium oleate. The effects of calcination temperature on the synthesis of CCNPs and CONPs were examined. Various characterization techniques were used to analyze the synthesized nanomaterials. The results showed that monodispersed CONPs could be efficiently prepared using calcium oleate, and they can be applied in various applications in a cheap and convenient manner.