Effects of Zr Content on the Microstructure of FeCrAl ODS Steels

期刊

METALS
卷 12, 期 7, 页码 -

出版社

MDPI
DOI: 10.3390/met12071114

关键词

FeCrAl ODS steels; Zr addition; grain size; second phases

资金

  1. Scientific Research Program for Young Talent of the China National Nuclear Corporation [NPIC-K301007033]

向作者/读者索取更多资源

The effects of Zr content on the grain size and precipitation of dispersed second phases in FeCrAl ODS steels were investigated. The results showed that the grain size decreased first and then increased as the Zr content increased, and the dispersed second phase changed from the Al2Y4O9 phase to the Y4Zr3O12 phase.
FeCrAl oxide dispersion strengthened (ODS) steels are an important kind of cladding material for accident-tolerant fuels. Their radiation resistance and mechanical properties are closely related to the grain size and dispersed second phases. In order to tailor the microstructure and provide an experimental basis for the composition design of FeCrAl ODS steels, in this paper FeCrAl ODS steels with different Zr contents were prepared by mechanical alloying and the subsequent hot isostatic pressing (MA-HIP) process. The effects of Zr content on the grain size distribution and the precipitation of dispersed second phases in FeCrAl ODS steels were investigated by electron back-scattered diffraction (EBSD) and transmission electron microscopy (TEM). The results showed that the grain size decreased first and then increased as the Zr content increased, and that the average grain size achieved the minimum value of 2.092 mu m when the Zr content was 0.6 wt.%. The Zr content had a negligible effect on the grain orientation of FeCrAl ODS steels, but the dispersed second phase changed from the Al2Y4O9 phase with monoclinic structure to the Y4Zr3O12 phase with hexagonal structure as the Zr content increased.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.5
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据