NANO LETTERS
卷 22, 期 12, 页码 4861-4869出版社
AMER CHEMICAL SOC
DOI: 10.1021/acs.nanolett.2c01243
关键词
lithium dendrites; functional separators; Prussian blue analogues; tuning metal ions; strong cationic sites; high-power lithium metal batteries
类别
资金
- National Natural Science Foundation of China [22005108]
- Natural Science Foundation of Guangdong Province [2019A1515011460, 2019B1515120027]
- Department of Science and Technology of Guangdong Province [2021A0505030063, 2020B0101030005, 2022B1515020005]
- special funds for science and technology innovation cultivation of undergraduate in Guangdong
By controlling Prussian blue analogues, the Li dendrite issue can be addressed, enabling high-power and long-lasting Li metal batteries at high current densities.
The Li dendrite issue is the major barrier that limits the implement of Li metal anode practically, especially at high current density. From the perspective of the nucleation and growth mechanism of the Li dendrite, we rationally develop a novel Prussian blue analogues (PBA)-derived separator, where tuning the metal ions bestows the PBAs with open metal site to confine anion movement and thereby afford a high Li+ transference number (0.78), and PBA with ordered micropores could act as an ionic sieve to selectively extract Li+ and thereby homogenize Li+ flux. This demonstrates a highly reversible Li plating/stripping cycling for 3000 h at a practically high current density (5.0 mA cm(-2)). Consequently, a high loading Li parallel to LiFeO4 battery (similar to 10.0 mg cm(-2)) demonstrates ultralong cycling life at high current densities (similar to 5.1 mA cm(-2)). This work highlights the prospect of optimizing PBAs in regulating ion transport behavior to enable high-power Li metal batteries.