The study investigated the effects of recrystallization annealing on the microstructure evolution and tensile behavior of Inconel 617B alloy pipes at 750°C. It was found that annealing temperature significantly impacted the grain size and grain growth rate, affecting both the strength and ductility of the alloy. Furthermore, the interaction between Cr-rich phases and dislocations played a crucial role in strengthening the alloy.
The effects of recrystallization annealing on the microstructure evolution of Inconel 617B alloy pipes and its tensile behavior at 750 ?C were investigated. As the annealing temperature increases, the grain size and grain growth rate increase dramatically due to the dissolution of the precipitated particles and the enhanced diffusion of solute atoms. Oil-quenched (OQ) samples generated evenly dispersed Cr-rich carbides with stacking faults (SFs) and Lomer-Cottrell (L-C) locks near the carbides, whereas water-quenched (WQ) samples had compara-tively clean grain boundaries and matrix. The interaction of Cr-rich phases and dislocations in the oil-quenched sample resulted in the strengthening of the alloy. Besides, because the precipitation of the Cr-rich phase led to the reduction of localized stacking fault energy (SFE), the alloy could coordinate the deformation by forming nano -deformation twins, which significantly improved the tensile ductility and allowed the alloy to have a larger work hardening index (n). At 1180 ?C, holding 4 min, then oil quenched annealing conditions, the sample achieved the excellent strength-elongation combination, i.e., the ultimate tensile strength (UTS) of 445 MPa and the elongation (EI) of 47.8% under tensile loading at 750 ?C, since the appropriate grain size cooperated with the precipitated phase. The stress concentration caused by the Cr-rich phase in the grain leads to cavitation nucleation. However, the cavitation nucleation at the triple junction of grain boundaries caused by the precipitation phase and grain boundary slips in the samples with other annealing conditions was still the foremost responsible for the fracture.