Dynamic compressive properties and microstructural evolution of Al1.19Co2CrFeNi1.81 eutectic high entropy alloy at room and cryogenic temperatures

期刊

MATERIALS & DESIGN
卷 219, 期 -, 页码 -

出版社

ELSEVIER SCI LTD
DOI: 10.1016/j.matdes.2022.110724

关键词

Eutectic high entropy alloy; Impact loading; Deformation mechanism; Nanotwins; Adiabatic shear band

资金

  1. Civil Aerospace Pre Research Project [D020304]

向作者/读者索取更多资源

The development of aerospace and military defense sectors has increased the demand for metals with enhanced mechanical properties under extreme conditions. Eutectic high entropy alloys (EHEAs) offer potential applications in these fields due to their excellent mechanical performance and good castability. In this study, the dynamic compressive properties and microstructural characteristics of Al1.19Co2CrFeNi1.81 EHEA were investigated at room temperature and liquid nitrogen temperature. The EHEA exhibited high strength and plasticity, particularly at liquid nitrogen temperature and high strain rate.
The development of aerospace and military defense sectors has put forward higher requirements for the mechanical properties of metals under extreme conditions. Eutectic high entropy alloys (EHEAs) show a wide potential application in these fields due to their superior mechanical performances and good castability. Here, we systematically investigated the dynamic compressive properties and microstructural characteristics of the Al1.19Co2CrFeNi1.81 EHEA at room temperature (298 K) and liquid nitrogen temperature (77 K). The EHEA exhibits an excellent strength-plasticity combination, especially at the strain rate of 4300 s(-1 )at 77 K, showing a yield strength of 1365 MPa and a true plastic strain over 40%. The underlying deformation mechanisms were uncovered using transmission electron microscopy, revealing that the deformation mechanism is dominated by dislocation slip at 298 K. However, at 77 K, nanotwins together with dislocation slip dominate the plastic deformation. Meanwhile, profuse relatively stable structures are formed due to the interactions between stacking fault (SF)-SF, dislocation-twin boundary and nanotwin-nanotwin, which can effectively inhibit dislocation movement and contribute to a superior strain hardening ability. The adiabatic shear band forms in the late stage of dynamic deformation, and the fractographic observations show a transition from ductile to mixed ductile-brittle fracture mode with decreasing temperature. (c) 2022 Published by Elsevier Ltd. This is an open access article under the CC BY-NC-ND license (http://creativecommons.org/licenses/by-nc-nd/4.0/).