This study investigates the hot deformation behavior and optimal process parameters of ASTM A335 P92 steel. It is found that the steel exhibits dynamic recovery behavior at high temperatures, and the flow stress decreases with increasing temperature or decreasing strain rate. The correlation between the constructed processing maps and microstructure provides guidance for selecting process parameters.
This article reports the flow stress behaviour of ASTM A335 P92 steel. Uniaxial isothermal compression experiments were conducted to examine the hot deformation behaviour of P92 steel in a Gleeble (R) 3500 thermal-mechanical simulator. The test conditions were 0.01-10 s(-1) strain rate and 850-1000 degrees C deformation temperature. Constitutive equations and processing maps developed were used to describe the hot deformation process. The results showed that the flow stress-strain curves exhibited a dynamic recovery (DRV) behaviour as the dominant softening mechanism. The flow stress decreased with an increase in the deformation temperature or a decrease in strain rate. Using the Arrhenius equation, the stress exponent and the activation energy values were 8.0 kJ.mol(-1) and 487.56 kJ.mol(-1), respectively. The correlation between the constructed processing maps and microstructure showed that the optimal process parameters occurred at a lower strain rate in the region of 0.1 s(-1) and deformation temperatures of 900-950 degrees C and 1000 degrees C for the steel investigated.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据