DIAMOND AND RELATED MATERIALS
卷 127, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.diamond.2022.109157
关键词
Gamma irradiation; ZnCo2O4; Reduced graphene oxide; Supercapacitor
ZnCo2O4-rGO nanohybrid was synthesized by a simple hydrothermal method and characterized by XRD, Raman spectroscopy, and SEM. The study found that gamma irradiation with 1.25 MeV improved the specific capacitance and stability of the material, while reducing charge transfer resistance. Thus, ZnCo2O4-rGO has the potential to be used as an electrode material for supercapacitors in gamma radiation environments.
ZnCo2O4-rGO nanohybrid was synthesized by a simple hydrothermal method. X-ray diffraction (XRD) and Raman spectroscopy analysis confirmed the successful synthesis of this nanomaterial. To study the morphology and thickness of the material, a scanning electron microscope (SEM) was prepared. For the application of this material as an electrode of supercapacitors, cyclic voltammetry (CV), galvanostatic charge-discharge (GCD), and electrochemical impedance spectroscopy (EIS) tests were performed. The novelty of this study was to investigate the effect of gamma-irradiation with 1.25 MeV average energy (Co-60) on the supercapacitor properties of electrodes. The synthesized samples were exposed to gamma rays at doses of 5, 10, 15, 25, and 50 kGy. The sample that was exposed to the highest amount of gamma radiation showed the highest specific capacitance 365 Fg(-1) and the maximum stability compared to other samples after 5000 consecutive cycles and the lowest charge transfer resistance. Discharge time was also increased in the gamma-ray exposed ZnCo2O4-rGO (50 kGy) by 88 s at a current density of 0.5 Ag-1 compared to the non-irradiation sample. According to these results, gamma ray not only has no destructive effect on electrode performance but also improves electrode performance. Thus, ZnCo2O4-rGO has the potential to be applied as the electrode material for supercapacitors in gamma radiation media.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据