期刊
JOURNAL OF COATINGS TECHNOLOGY AND RESEARCH
卷 14, 期 1, 页码 85-94出版社
SPRINGER
DOI: 10.1007/s11998-016-9830-4
关键词
Corrosion resistance; Silica nanocapsules; Corrosion inhibitor; Sol-gel coatings; Aluminum
资金
- National Natural Science Foundation of China [51302253]
This work presents the synthesis of corrosion inhibitor [1H-benzotriazole (BTA)]-loaded hollow silica nanocapsules with magnesium hydroxide precipitate in the shells (HSNs-M/BTA) through inverse microemulsion (W/O) polymerization. TEM and Brunauer-Emmett-Teller (BET) measurements indicate that the silica nanocapsules possess voids in the inner part and mesoporous on the surface. The actual loading capacity of BTA is 287.17 mg (BTA)/1 g (HSNs-M/BTA). The results of UV absorption spectra show that the release of BTA can be triggered by the changing of pH in the corrosion solution. The anticorrosive SiO (x) /ZrO (x) coatings embedded with hydrophobically modified HSNs-M have a better waterproof performance since the water contact angle can reach 140A degrees. In comparison to the passive SiO (x) /ZrO (x) coatings with or without BTA, the enhanced corrosion protection performance of this developed anticorrosive system was observed by both electrochemical impedance spectroscopy and Tafel analysis. The fabrication of nanocapsules with corrosion inhibitors is promising as an intelligent element in protective coatings in the future.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据