adsorption heat transformation; UiO-66; water vapor adsorption; MgCl2
资金
- National Natural Science Foundation of China
- [51836009]
This study presents the modification of UiO-66 with MgCl2 to enhance its water vapor adsorption performance and heat storage capacity. The introduction of MgCl2 improves the water adsorption capacity of UiO-66, despite reducing its specific surface area and pore volume.
UiO-66 is a potential material for adsorption heat transformation (AHT) with high specific surface area, and excellent thermal and chemical stability. However, the low water adsorption capacity of UiO-66 in the low relative pressure range (0 < P/P (0) < 0.3) limits its application in AHT. We prepare the UiO-66 modified by MgCl2 through using the solvothermal method and impregnation method, and study their water vapor adsorption performances and heat storage capacities. Attributed to the extremely high saturated water uptake and excellent hydrophilicity of MgCl2, the water adsorption performance of UiO-66 is improved, although the introduction of MgCl2 reduces its specific surface area and pore volume. The water adsorption capacity at P/P (0) = 0.3 and the saturated water adsorption capacity of the UiO-66 (with MgCl2 content of 0.57 wt%) modified by the solvothermal method are 0.27 g/g and 0.57 g/g at 298 K, respectively, which are 68.8% and 32.6% higher than the counterparts of pure UiO-66, respectively. Comparing with pure UiO-66, the water adsorption capacity of the UiO-66 (with MgCl2 content of 1.02 wt%) modified by the impregnation method is increased by 56.3% and 14.0% at the same pressure, respectively. During 20 water adsorption/desorption cycles, the above two materials show high heat storage densities (similar to 1293 J/g and 1378 J/g). Therein, the UiO-66 modified by the solvothermal method exhibits the excellent cyclic stability. These results suggest that the introduction of an appropriate amount of MgCl2 makes UiO-66 more suitable for AHT applications.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据