Blue CsPbBr3 nanoplates; Low-temperature synthesis; High PLQY; LEDs; Spectral stability
资金
- Natural Science Foundation of Shandong Province [ZR2021MF029, ZR2017PF012, ZR2019MA066, ZR2020MF103]
- Taishan scholar Project of Shan-dong Province [tsqn201812098]
This study successfully fabricated high-efficiency blue LEDs using low-temperature synthesis of CsPbBr3 nanoplates, demonstrating advantages such as high quantum efficiency, stable spectral characteristics, and tunable color range.
Despite heavy research, the efficiencies of blue perovskite light-emitting diodes (LEDs) lag behind those of their green and red cousins. One of the most critical problems is the lack of technology to obtain both high blue emission and spectral stability of perovskite in thin films. Herein, we employ low-temperature synthesis of CsPbBr3 nanoplates (NPLs) by anti-solvent assisted crystallization method using green ethylacetate anti-solvent, which show high absolute photoluminescence quantum yield (PLQY = 90.2%), blue emission at 464 nm with a narrow emission line width (15 nm), small Stokes shift (5 nm) and the average PL decay lifetime (6.91 ns). Significantly, there is no obvious QY loss at different storage conditions. Furthermore, the PL can be tuned from blue to green (457-513 nm) by controlling the amount of precursor injected into anti-solvent. For the first time, we utilize all-bromide-based inorganic perovskites to fabricate ultraviolet-pumped white LEDs (UV-WLEDs) and optimize the chromaticity coordinate of WLEDs, whose CIE color temperature (CCT) is 6083 K. Finally, highly efficient blue LED device using CsPbBr3 nanoplates (464 nm) with high external quantum efficiency (EQE) of 2.03% was fabricated and spectral stability of CsPbBr3 nanoplates under constant current density was demonstrated. This work will be expected to facilitate the development of the blue light source for WLEDs and displays.