Lithium metal battery; Limited anode; High voltage; High loading cathode; Flame retardant
类别
资金
- National Natural Science Foundation of China [52072322]
- Department of Science and Technology of Sichuan Province (CN) [22ZDYF2703, 2019-GH02-00052-HZ]
- Young scholars development fund of SWPU [202199010143]
- Scientific research starting project of SWPU [2021QHZ039]
A novel flame retardant fluorine-rich electrolyte (FFT) was designed and studied in this research, which exhibited noninflammability, low viscosity, good wettability and fluidity, and high oxidation stability. The electrolyte enabled high-energy density lithium metal batteries to maintain good capacity performance and exhibited excellent discharge capacity at low temperatures.
Traditional carbonate-based electrolytes are not suitable for high voltage lithium metal batteries (LMBs), which seriously hinders the development of high-energy density LMBs. Here, a novel flame retardant fluorine-rich electrolyte (termed FFT) composed of 1.2 M lithium hexafluorophosphate (LiPF6) in a mixed solvents of fluoroethylene carbonate (FEC), 3,3,3-fluoroethylmethyl carbonate (FEMC) and 1,1,2,2-tetrafluoroethyl-2,2,3,3-tetrafluoropropyl ether (TTE) was rationally designed and studied. It exhibits noninflammability, low viscosity, good wettability and fluidity, and high oxidation stability. The designed electrolyte enables Li||NMC622 with limited Li anode (50 mu m thickness) and high cathode active material loading of 13.8 mg cm-2 (2.5 mAh cm(-2)) to remain 80% capacity after 160 cycles and 135 cycles with a high cut-off of 4.4 V and 4.5 V under charge at C/5 and discharge at C/2 at 25 ?, respectively. Moreover, the Li||NMC622 using FFT also exhibits excellent low temperature discharge capacity, which could deliver 122 mAh g(-1) (about 62% of the discharge capacity at 25 ?) even at-40 ?. Further analyses reveal the stable and conductive CEI and SEI with LiF-rich are formed on both cathode and anode, which contributes to the stable cycle of the battery.