4.8 Article

Stress-Regulation Design of Lithium Alloy Electrode toward Stable Battery Cycling

期刊

ENERGY & ENVIRONMENTAL MATERIALS
卷 6, 期 1, 页码 -

出版社

WILEY
DOI: 10.1002/eem2.12267

关键词

chemo-mechanical simulation; lithium alloy; lithium-ion batteries; mechanical lithography; stress regulation

向作者/读者索取更多资源

A GeSn electrode with an undulating structure was fabricated and shown to improve the mechanical stability, homogenize electrochemical reactions, and compensate for lithium loss, resulting in enhanced electrochemical performance. Experimental results from symmetric cells and full cells demonstrated the feasibility and superiority of the GeSn electrode.
Metallic tin (Sn) foil is a promising candidate anode for lithium-ion batteries (LIBs) due to its metallurgical processability and high capacity. However, it suffers low initial Coulombic efficiency and inferior cycling stability due to its uneven alloying/dealloying reactions, large volume change and stress, and fast electrode structural degradation. Herein, we report an undulating LiSn electrode fabricated by a scalable two-step procedure involving mechanical lithography and chemical prelithiation of Sn foil. With the combination of experimental measurements and chemo-mechanical simulations, it was revealed the obtained undulating LiSn/Sn electrode could ensure better mechanical stability due to the pre-swelling state from Sn to LixSn and undulating structure of lithography in comparison with plane Sn, homogenize the electrochemical alloying/dealloying reactions due to the activated surface materials, and compensate Li loss during cycling due to the introduction of excess Li from LixSn, thus enabling enhanced electrochemical performance. Symmetric cells consisting of undulating LiSn/Sn electrode with an active thickness of similar to 5 um displayed stable cycling over 1000 h at 1 mA cm(-2) and 1 mAh cm(-2) with a low average overpotential of <15 mV. When paired with commercial LiNi0.6Co0.2Mn0.2O2 (NCM622) cathode with high mass loading of 15.8 mg cm(-2), the full cell demonstrated a high capacity of 2.4 mAh cm(-2) and outstanding cycling stability with 84.9% capacity retention at 0.5 C after 100 cycles. This work presents an advanced LiSn electrode with stress-regulation design toward high-performance LIBs, and sheds light on the rational electrode design and processing of other high-capacity lithium alloy anodes.

作者

我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。

评论

主要评分

4.8
评分不足

次要评分

新颖性
-
重要性
-
科学严谨性
-
评价这篇论文

推荐

暂无数据
暂无数据