Photocatalytic activity; Rutile TiO 2; Arc discharge; Surface OH groups; Defects
资金
- Tarbiat Modares University [IG-39703]
This research focuses on the preparation of defective rutile TiO2 nanoparticles with highly efficient photocatalytic activity under visible light. The synthesis method involves electric arc discharge in water followed by heat treatment. The study provides evidence for the improvement of photocatalytic activity through the introduction of oxygen vacancies. The annealing temperature affects the particle size and optical band gap of the TiO2 nanoparticles, and the concentration of non-lattice oxygen influences the degradation efficiency.
Preparation of the defective TiO2 nanoparticles (NPs) have been recently in particular in -terest for its outstanding applications in visible-light active photocatalysis. In order to make TiO2 visible-light absorber, optical band gap should be modified especially via introducing structural defects like oxygen vacancies as an effective pathway. In this research, we prepared defective rutile TiO2 NPs with highly efficient photocatalytic activity under visible light. The NPs were synthesized by electric arc discharge in water as a cost-effective and environmentally friendly method with capability of defect formation which followed by heat treatment. The photocatalytic activity improvement mechanisms based on oxygen vacancies were supported by TEM, XPS, XRD, PL and optical spectroscopy characterizations. Spherical TiO2 NPs with average size of 23, 28, 38, and 50 nm were ob-tained for pristine, and annealed samples at 300, 500 and 700 & DEG;C respectively. The optical band gaps of NPs decreased from 2.9 to 2.0 eV with annealing temperature, and a con-current color change from blue-gray to light-gray. The XPS results confirm the presence of vacant oxygen and surface OH defects in all TiO2 samples. The results reveal that con-centration of surface defects and mostly the oxygen vacancies play a crucial role in visible light photoactivity of gray TiO2 nanostructures. In the synthesized TiO2 NPs, the sample with the lowest concentration of non-lattice oxygen exhibit better degradation efficiency than other samples. The results provide a flexible method for synthesis of defective rutile TiO2 as a highly efficient visible active photocatalyst nanomaterial.(C) 2022 The Author(s). Published by Elsevier B.V.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据