DOI: 10.3390/met12030530
关键词
GMAW-P-brazing; microstructure; CP steel; mechanical properties; zinc
资金
- CONACyT-Mexico
- Coordinacion de la Investigacion Cientifica of Universidad Michoacana de San Nicolas de Hidalgo
In this study, joints of complex phase 780 advanced high strength steel were welded using different welding processes. The results showed that the joints welded with GMAW-P-brazing process exhibited significantly higher tensile strength compared to those welded with GMAW-P process. The study also found that there was higher evaporation of zinc in the GMAW-P process.
Joints of complex phase 780 (CP-780) advanced high strength steel (AHSS) were carried out by using an ER-CuAl-A2 filler metal for the gas metal arc welding pulsed brazing (GMAW-P-brazing) process and the ER-80S-D2 for the GMAW-P process employing two levels of heat input. The phases in the weld bead and HAZ were analyzed, and the evaporation of zinc by means of scanning electron microscopy (SEM) was also monitored. The mechanical properties of the welded joints were evaluated by tension, microhardness and vertical impact tests. It was found that there was greater surface Zn evaporation in the joints welded with the GMAW-P process as compared to the GMAW-P-brazing process. The best results in tensile strength were observed in the joints welded with GMAW-P-brazing process, which increased by similar to 68% with respect to those of the GMAW-P. This behavior can be attributed to the formation of an intermetallic complex compound Cu-Al-Fe in the fusion line.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据