The research aimed to investigate the ideal resin coating for mild steel surfaces and compared the corrosion rates and mechanical properties of epoxy, polyurethane, polyester, and phenolic resins. The results showed that epoxy resin was the most effective corrosion-resistant material.
The primary objective of the research was to investigate the ideal resin coating on the mild steel surface among various resin coatings which are in use. These resin coatings are used as an anti-corrosive material for mild steel surfaces with enhanced mechanical properties. The resins (epoxy, polyurethane, polyester, and phenolic) on mild steel surface were applied by the pneumatic spray coating method. In addition, immersion test and salt spray test methods were followed using sodium chloride (NaCl) solution. Furthermore, the rate of corrosion and mechanical properties of mild steel coated with different resins was evaluated by conducting various experiments (immersion test, salt spray test, tensile strength test, and scratch hardness test) and was compared with a bare mild steel surface. The results of the current research showed that the mild steel surface coated with epoxy resin was found to be the most effective corrosion resistance material with better mechanical properties compared to other tested mild steel resin-coated surfaces.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据