Characterization on the Copolymerization Resin between Bayberry (Myrica rubra) Tannin and Pre-Polymers of Conventional Urea-Formaldehyde Resin

By focusing on the disadvantages of weak water resistance and high formaldehyde emission of urea-formaldehyde resin (UF), this research provides a new method to overcome these shortages of UF resin by using tannin for partial substitution of urea. Furthermore, plasma pretreatment of wood was introduced to strengthen the bonding performance of plywood. The investigation of the chemical structure of UF resin and tannin-urea-formaldehyde resin (TUF) were performed with Fourier transform infrared spectroscopy (FT-IR) and solid-state C-13 nuclear magnetic resonance (C-13 NMR). The results of investigations confirmed the joining of tannin into the resin structure, which may enhance structural rigidity of TUF adhesives and improve hydrolysis stability. Then, thermal performance of UF resin and TUF resins were tested by differential scanning calorimetry (DSC) and thermogravimetric (TG) analysis. The DSC results indicated that the curing temperature did not change significantly. However, the TG analysis showed that the thermal stability of TUF resin was considerably improved. In bonding performance test, tannin-urea-formaldehyde resin (TUF) revealed an excellent water resistance, comparable to UF resin and can fulfill the standard requirement for plywood (Type II according to the Norm GB/T 17657-2013). It is interesting that the shear strength of wood specimens, bonded with TUF6 resin, after low-pressure cold plasma equipment (CLP plasma) and jet type atmospheric low-temperature plasma (JTLP plasma) treatment, reached 0.80 MPa and 0.85 MPa, respectively, after being soaked in boiling water for 3 h. In addition, most of the bonded plywood samples with TUF resin exhibited a lower formaldehyde emission, especially those prepared at 70 degrees C and 1.5 h, in which the formaldehyde emission amount could be reduced by approximately 39%.

Automated summary

This research focuses on overcoming the disadvantages of weak water resistance and high formaldehyde emission of urea-formaldehyde resin (UF) by partially substituting urea with tannin. Plasma pretreatment of wood is introduced to enhance the bonding performance of plywood. The results show that tannin-urea-formaldehyde resin (TUF) has improved water resistance and reduced formaldehyde emission.