DOI: 10.3390/ma15093121
关键词
closed coil springs; nickel-titanium; orthodontics; superelasticity; thermo-mechanical properties
This research aimed to determine the optimal heat treatment temperature and duration for NiTi-closed coil springs, revealing that heat treatment at 500 degrees Celsius for 40 minutes can produce appropriate force delivery levels with lower plateau slope and less hysteresis for orthodontic use.
Nickel-Titanium (NiTi) springs have been increasingly used in orthodontics; however, no optimum condition of heat treatment has been reported. Therefore, this research was conducted to determine the optimum heat-treatment temperature and duration for the fabrication of NiTi-closed coil springs by investigating their effects on thermo-mechanical properties. As-drawn straight NiTi wires of 0.2 mm diameter were used to fabricate closed coil springs of 0.9 mm lumen diameter. The springs were heat-treated at three different temperatures (400, 450, and 500 degrees C) with three different durations (20, 40, and 60 min). Electron Probe Micro-Analysis (EPMA) and Differential Scanning Calorimetry (DSC) were used to investigate element composition and thermo-mechanical properties, respectively. Custom-made NiTi closed coil springs composed of 49.41%-Ti and 50.57%-Ni by atomic weight, where their DSC curves of 500 degrees C presented the obvious endothermic and exothermic peaks, and the austenite finish temperature (A(f)) were approximately 25 degrees C. With increasing temperature, deactivation curves presented decreased plateau slopes generating higher superelastic ratios (SE ratios). At 500 degrees C, closed coil springs showed superelastic tendency with lower stress hysteresis. The thermo-mechanical properties were significantly influenced by heat-treatment temperature rather than duration. The optimum parameter appeared to be 500 degrees C for 40 min to produce appropriate force delivery levels, relatively low plateau slope, and lower hysteresis for orthodontic use.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据