期刊
SEPARATION AND PURIFICATION TECHNOLOGY
卷 286, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.seppur.2022.120504
关键词
Cellulose membrane; Superhydrophobicity; Harsh environment; Photocatalytic degradation; Oil/water separation ; Biofouling
资金
- National Natural Science Foundation of China [11864024]
- Jiangxi Provincial Natural Science Foundation [20202BABL214025]
- Key Project of Key Research and Development Program of Jiangxi Province [20212BBE51021]
- Young Jinggang scholar of Jiangxi Province
- Qing Lan Project of Jiangsu Province
In this study, MnO2 micro/nanoparticles were successfully deposited on the cellulose-based membrane surface, followed by decoration with stearic acid, resulting in a superhydrophobic CM sample with excellent oil/water separation, anti-fouling, and dye photodegradation properties triggered by visible light.
Flexible multiple functional cellulose-based membrane (CM) for oil/water separation, anti-microbial and photodegradation are in great demand in marine wastewater treatment due to its' effective and ecologically benign. Based on this requirement, MnO2 micro/nanoparticles were in situ deposited on CM sample surface followed by decoration of stearic acid (STA) for very effective oil/water separation, anti-fouling, and dye photodegradation triggered by visible light. The results demonstrated that this as-prepared CM sample showed super hydrophobicity with a water contact angle of 162 +/- 2? and superoleophilicity with an oil contact angle of 0?. It also demonstrated exceptional high stability in hostile environments (acid and alkali solution, high temperature, wear resistance, underwater writing, self-cleaning) and a 2.6% increase in tensile strength. In addition, it can successfully separate emulsified oils from typical oil-in-water emulsions with good separation efficiency all over 98% and comparatively high flux (145.8 L.m(-2).h(-1)). After 8 cycles, the separation efficiency of the n-hexane/ water emulsion is still over 98%. Moreover, over 98% of MB was degraded by using superhydrophobic CM sample, indicating strong photocatalytic activity. Meanwhile, in the maritime environment, this biomimetic sample decreased the adherence of green algae by more than 95%, demonstrating strong anti-biofouling adhesion potential. It indicates that this cost-effective, scalable, environmental friendly, and efficient methodology presented superhydrophobic CM sample has the potential to promote the widespread development of multipurpose superwetting materials, with enticing potential for the treatment of complex oily wastewater.