期刊
POWDER TECHNOLOGY
卷 402, 期 -, 页码 -出版社
ELSEVIER
DOI: 10.1016/j.powtec.2022.117331
关键词
Alginate; Aerogel particle; Coating; Polymer; Wurster fluidized bed
资金
- Kog University Surface Science and Technologies Center (KUYTAM)
Alginate aerogel particles were successfully coated with a copovidone and hydroxypropyl cellulose based polymer in a Wurster fluidized bed. The results indicate that the pores of aerogels were not damaged during the process. Changing bed temperature led to significant changes in coating thickness whereas both bed temperature and atomizing pressure affected coating layer surface morphology. The smoothest coating layer surface and the highest coating efficiency were achieved at 50 degrees C with 1.7 bar atomizing pressure.
Alginate aerogel particles were successfully coated with a copovidone and hydroxypropyl cellulose based polymer in a Wurster fluidized bed. The results indicate that the pores of aerogels were not damaged during the process. Several sets of experiments were conducted at three different temperatures and atomizing air pressures. Coating time for all the runs ranged from 5 min to 40 min and the coating thickness ranged from 12.4 +/- 4.6 mu m to 170.6 +/- 43.3 mu m.Changing bed temperature led to significant changes in coating thickness whereas both bed temperature and atomizing pressure affected coating layer surface morphology. The smoothest coating layer surface and the highest coating efficiency which was 69.2 +/- 0.4% were achieved at 50 degrees C with 1.7 bar atomizing pressure. At this condition, the coating layer thickness increased linearly with coating time.(c) 2022 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据