Spray pyrolysis developed Nd doped Co3O4 nanostructured thin films and their structural, and opto-nonlinear properties for optoelectronics applications

Herein we are reporting the facile spray pyrolysis fabrication of different Neodymium (Nd) contents loaded cobalt oxide (Co3O4) nanostructured thin films at 400 degrees C substrate temperature and investigated for optononlinear applications. Structural and vibrational studies approve the cubic system of all films with the low crystallite size between 25 and 20 nm. FESEM e-mapping and EDX analyses further confirm the homogeneous Nd doping in Co3O4 films. FESEM study reveals that the grains are very fine and distributed throughout the films. The optical study reveals that the grown films possess two energy gaps which are between 2.03 and 2.15 eV and 1.49-1.55 eV. Photoluminescence study has been performed at three different excitation wavelengths and the mono-emission was noticed at 375, 500 and 754 nm. Furthermore, the linear absorption and refractive indices were determined along with dielectric and electrical properties. Also, the nonlinear susceptibility and refractive index were determined and found to be in range of 4 x 10(-13) to 1.27 x 10(-10) esu and 5.86 x 10(-12) to 1.35 x 10(-9) esu., respectively.

Automated summary

In this study, different Neodymium contents loaded cobalt oxide nanostructured thin films were fabricated using facile spray pyrolysis method, and their structural, optical, and electrical properties were investigated.