MATERIALS CHEMISTRY AND PHYSICS
卷 282, 期 -, 页码 -出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.matchemphys.2022.125916
关键词
Spintronics; Sol-gel spin coating; Ferromagnetism; Mn-doped NiO thin Films; Bound magnetic polaron
资金
- University of Kerala, Thiruvananthapuram, Kerala, India
The research investigated the structural, morphological, optical, and magnetic properties of Mn-doped NiO thin films, revealing that Mn doping alters the lattice parameters and introduces strain in NiO films, while increasing Mn content decreases the intensity of the Photoluminescence spectra.
Manganese (Mn)-doped Nickel (II) Oxide (NiO) thin films are prepared using sol-gel spin coating method. The structural, morphological, optical, and magnetic properties of these films are studied using XRD, FE-SEM, Micro Raman spectroscopy, UV-visible spectroscopy, Photoluminescence (PL) spectroscopy, and VSM analysis. XRD results reveals that doping of Mn retains the cubic phase of NiO but changes its lattice parameters and introduces strain in the NiO films. The crystallite size of NiO films decreases from 19.86 nm to 12.11nm as the doping concentration of Mn changes from 0 to 15 mol%. XPS and Micro-Raman spectrum confirm the successful incorporation of Mn ions into NiO. The intensity of the PL spectra decreases with increasing Mn content. The violet, blue, and green emissions in the luminescence spectrum indicate the presence of vacancy defects corresponding to nickel and oxygen. Our research shows that these defects influence the magnetic properties of the doped thin films of NiO. The results from the vibrating sample magnetometer (VSM) explain the ferromagnetic behavior of the Mn doped NiO thin films.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据