期刊
JOURNAL OF ALLOYS AND COMPOUNDS
卷 667, 期 -, 页码 287-296出版社
ELSEVIER SCIENCE SA
DOI: 10.1016/j.jallcom.2016.01.175
关键词
Nickel; Microporous nanoparticles; Core/shell structure; Microwave absorption
资金
- National Natural Science Foundation of China [U1560106]
- Aeronautical Science Foundation of China [2014ZF51069]
- Scientific Research Foundation for the Returned Overseas Chinese Scholars, State Education Ministry
The fabrication of microporous metal materials with many potential applications is challenging due to their high chemical activities and the difficulty in controlling the pore size. By adjusting the reaction condition and the composition of the Ni-Al nanoparticle precursor, we have successfully produced the microporous Ni nanoparticles (NPs) of 22 nm by chemical dealloying method. During the passivation process, the microporous Ni NPs covered with NiO shell are generated as the result of surface oxidation. The micropores range from 0.6 to 1.2 nm in diameter with a large surface area of 68.9 m(2)/g. Due to the elimination of Al atoms during dealloying process, the crystalline size of the microporous Ni NPs is sharply decreased to 2-5 nm. The specific architecture offers the microporous Ni/NiO NPs a small microwave reflection coefficient (RC) and a wide absorption bandwidth (RC <= -10 dB) of -49.1 dB and 5.8 GHz, much better than the nonporous counterpart of -24.1 dB and 3.7 GHz. The enhanced microwave absorption performance has been interpreted in terms of the micropore structure, core/shell structure and nanostructure effects. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据