High cycle fatigue; Ti-6.5Al-2.2Mo-2.2Zr-1.8Sn-0.7W-0.2Si; Equiaxed microstructure; Bi-modal microstructure; Full lamellar microstructure
资金
- Research Fund for the Doctoral Program of Higher Education of China [20116102110015]
- New Century Excellent Talents in University [NCET-07-0696]
The high cycle fatigue properties of Ti-6.5Al-2.2Mo-2.2Zr-1.8Sn-0.7W-0.2Si with three typical microstructures (equiaxed, bimodal and full lamellar) prepared by carefully controlled isothermal forging and heat treatment procedures are investigated by comparison. Equiaxed and bimodal microstructures exhibit a higher HCF resistance than the full lamellar one and a mismatching of HCF strength with yield strength for equiaxed and bimodal microstructures is observed. Fractography analysis shows crack initiates primarily at the subsurface of similar to 30 mu m-300 mu m for the three microstructures. Interior initiation occurs in 5 specimens of the 19 specimens that were measured. For equiaxed and bi-modal microstructures, the interior initiation samples have significant higher fatigue life than those initiated at (sub) surface under the same fatigue stress, while in lamellar structure, the initiation location shows no such effect on fatigue life. It is found that two factors, i.e. the effective slip length and the intrinsic strength, jointly decide the fatigue crack initiation in the present alloy. The dependence of crack initiation on microstructure is responsible for the microstructural sensitivity of HCF properties. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据