Forging; Mg-Gd-Y-Zr alloy; Superplasticity; Recrystallization
资金
- National Natural Science Foundation of China (NSFC) [51301173, 51531002]
- National Basic Research Program of China (973 Program) [2013CB632202]
A novel multi-directional impact forging (MDIF) process was successfully applied to a Mg-Gd-Y-Zr alloy and the superplasticity of the MDIFed alloy was investigated. It was shown that the initial microstructure after MDIF had a unique characteristic of coarse grains decorated by profuse tension twins. Tensile tests at various temperatures and initial strain rates displayed that the MDIFed alloy exhibited superplasticity at temperatures higher than 400 degrees C, especially the maximum elongation of about 300% was achieved at 450 degrees C and 5 x 10(-4) s(-1). It was observed that the initial twin lamellas diminished and even vanished with the occurrence of static recrystallization (SRX) during preheating. The detailed microstructural analysis revealed that SRX during preheating and dynamic recrystallization (DRX) during tensile testing conduced to the superplasticity. With strain rate sensitivity exponent m-value of about 0.32, the superplastic deformation mechanism was supposed to be predominated by glide-controlled dislocation creep assisted by grain boundaries sliding. (C) 2016 Elsevier B.V. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据