Sub-1 nm pore; Porous carbon; Facile method; Energy density; Supercapacitor
资金
- Faculty of Materials and Energy, Southwest University, Chongqing of China
- Suzhou University of Science and Technology, Suzhou of China
- Innovation Platform for Academicians of Hainan Province
The study successfully prepared sub-1 nm pore-rich carbon material from biomass waste, which exhibits high specific capacitance, excellent rate capability, and long cyclic life. It shows great potential for practical applications in commercial supercapacitors.
Sub-1 nm pores can lead to an anomalous increase in the supercapacitive performance [1], but it still faces great challenges from its relatively low sub-1 nm pore content, complicated preparation process, low yield and high cost. Here we successfully prepared a sub-1 nm pore-rich carbon from biomass wastes using a facile method by pre-treating walnut shell powder at 380 degrees C in air for different times to delicately tailor carbon defects, followed by KOH activation at 700 degrees C. The as-prepared optimal material delivers the highest sub-1 nm pore content (Vsub-1 nm = 0.57 cm(3) g(-1), Vsub-1 nm/V-t = 58.4 %) among all reported porous carbons. A supercapacitor made from the material accomplishes an ultrahigh specific capacitance of 298.7F g(-1) at 1 A g(-1) in a two-electrode device, excellent rate capability (78.8 % retention from 1 to 10 A g(-1)) and long-cyclic life (94 % retention after 10,000 cycles at 10 A g(-1)) in KOH. Even in Et4NBF4 electrolyte that is often used in commercial supercapacitors, a high energy density of 82.8 Wh kg(-1) at 7 kW kg(-1) and excellent cycling performance (90 % retention after 10,000 cycles at 5 A g(-1)) can be achieved, ranking the best among all reported carbon-based electrical double layer capacitors tested in the same electrolyte. More importantly, it drives a light-emitting-diode (LED) to operate for as long as 20 min, vividly demonstrating the great potential of sub-1 nm pore-rich carbon-based high performance supercapacitors in practical applications. (C) 2021 Elsevier Inc. All rights reserved.