By preparing Mg90Ce3Ni7 alloy through medium-frequency induction melting and mechanical ball-milling process, the study found that ball-milling improves the hydrogen storage performance of the alloy by changing its microstructure. The alloy milled for 20 hours can absorb over 3.5 wt % of hydrogen within 30 minutes at 100 degrees C, indicating its potential for practical applications.
Aiming at improving hydrogen storage performance of Mg-base alloy, the Mg90Ce3Ni7 alloy is prepared by medium-frequency induction melting and following mechanical ball-milling process. X-ray diffraction analysis reveals that the ball-milling Mg90Ce3Ni7 alloy is composed of Mg, Mg2Ni and CeMg12 phases, whereas subsequent milling induces grain refinement and the formation of amorphous phase. In addition, the extension of ball-milling time also not further improve the thermodynamic properties, whereas has a very significant effect on the kinetic properties, which is mainly attributed to the change of microstructure of the alloy by ball milling process. The ball-milling not only creates the nanocrystalline and amorphous structures, but also refines the particle size of the alloy. This is beneficial to the nucleation and diffusion of the alloy during reversible hydroge-nation reaction. Concretely, the ball-milling time enhances the kinetics of hydrogen ab-sorption at low temperature, especially for the alloy milled for 20 h, in which can absorb more than 3.5 wt % H2 over 30 min at 100 degrees C. Meanwhile, the ball-milling time enhances the kinetics of hydrogen desorption. It leads to effectively reducing the dehydrogenation activation energy to 72.2 kJ/mol H2, which allows the alloy can release more than 5 wt % H2 in 10 min at 280 degrees C. The work provides a scientific way to promote the practical application of Mg-based hydrogen storage alloy.(c) 2022 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.
作者
我是这篇论文的作者
点击您的名字以认领此论文并将其添加到您的个人资料中。
推荐
暂无数据